Konpozisyon teknik tipik

Min. pousan

Max. pousan

Abityèl pousan

SiO₂

70

77

74.9

Al₂O₃

17

19

18

Fe₂O₃

******

1.0

0.9

TiO₂

******

0.5

0.46

CaO

******

0.5

0.42

MgO

******

0.5

0.38

Na₂O

******

2

1.12

 K₂O

******

3.5

3.28

Al₂O₃plis SiO₂

90

96

93

Pwopriyete fizik

Endèks

Valè

Valè

Leachable Iron

Mwens pase oswa egal a 0.1 pousan

******

Porosite aparan pa pwa, dia. Pi gran pase oswa egal a 10mm

Mwens pase oswa egal a 0.4 pousan

******

Porosite aparan pa pwa, dia.=6mm

Mwens pase oswa egal a 1.0 pousan

******

Porosite aparan pa pwa, dia.=3mm

Mwens pase oswa egal a 3.0 pousan

******

Echèl dite Moh a

>6.5

******

Absòpsyon dlo

<>

******

Rezistans asid

>99.8 pousan

******

Rezistans alkalin

>85 pousan

******

Kondiktivite tèmik

0.9-1.0 w/m².k

******

Ekspansyon tèmik @ 500degre

0.20 pousan

******

Espesifik Chalè

628-837 j/kg

******

Estabilite chòk tèmik, 500degreLè sa a, refwadisman dlo

10 fwa

******

Max. Tanperati Fonksyònman

1050degre

1922

Dansite espesifik

2300 kg/m³

144 lb/pye³

Dansite esansyèl (Dansite anbalaj)

1350 g / cm³

84 liv/pye³

Gwosè

Fòs kraze

Gwosè Nominal

(laj)

(KG)

(N/pc)

manm

Pous

min.

min.

min.

3

1/8

77

35

343

6

1/4

176

80

784

10

3/8

234

106

1039

13

1/2

572

260

2548

16

5/8

726

330

3234

19

3/4

1672

760

7448

25

1

1870

850

8330

38

1.5

2090

950

9310

50

2

3476

1580

15484

Aplikasyon tipik

a)Lajman itilize medya sipò nan mond lan paske nan konsistans ekselan yo ak fyab.

b) Manifaktire soti nan materyèl ajil chimik-porselèn bon jan kalite trè wo, ki gen estabilite trè ekselan, segondè fòs mekanik ak rezistans nan chòk tèmik, Sa fè yo tout chwa ideyal pou sipò nan

tout kalite katalis.

Garanti:

a) Dapre National Standard HG/T 3683.1-2000
b) Ofri konsiltasyon pou tout lavi sou pwoblèm ki te fèt